Treatment Analysis of Welding Structure in the Presence of a Crack Type Defects
The largest number of welded structures in operating conditions is exposed to variable loads, which is why the share of fatigue fracture in the failure of welded structures is higher than others. The essence of construction with fracture safety is that the structure can withstand the designed load in the designed time. If a crack is detected during operation, it is possible to predict the development of damage during the service life as well as the load-bearing capacity of the structure depending on the development of damage. The paper describes a new system for monitoring fatigue crack growth, which is based on the change in the resistance of the measuring foil during crack growth. The system is compatible with the basic settings of the ASTM E647–86 standard, which refers to the determination of the fatigue crack growth rate.