A. Alil, Stanica Nedović, S. Martinović, T. Volkov-Husović
0 2024.

Cavitation erosion monitoring of 42CrMo4 steel samples using the image and morphological analysis

The choice of steel depends on environmental factors like temperature, pressure, and chemical exposure. Steel components in machinery often face varying conditions that can lead to damage, such as cavitation erosion. In this study, steel 42CrMo4 samples were chosen to represent a common and widely used steel. Application of this type of steel is often related to the statically and dynamically stressed components for vehicles, engines, and machines, where corrosion or cavitation can occur. The behavior of steel samples under conditions of cavitation erosion in distilled water was the focus of this paper. Testing was performed using a standard cavitation vibratory setup using a stationary specimen, according to the ASTM G-32 procedure. Image and morphological analyses were implemented to quantify the level of sample degradation caused by cavitation. The observed changes in the monitored parameters during testing are linked to the degradation mechanism of cavitation erosion. The results showed that pits began forming within 60 minutes, and afterward, the growth and merging of these pits significantly impacted the degradation process.

Pretplatite se na novosti o BH Akademskom Imeniku

Ova stranica koristi kolačiće da bi vam pružila najbolje iskustvo

Saznaj više