Preparation and properties of low cement castable sintered at different temperatures
The low cement high alumina castable (LCC) studied in this paper was synthesised, cured and then treated at different sintering temperatures. Since any inhomogeneity introduced during the castable preparation can remain inside the material degrading its properties and therefore the quality during service life, particular attention was given to the processing procedure in order to produce the material with the optimum characteristics. Composition of the castable regarding particle size distribution was adjusted according to the Andreassen’s packing model. The samples were sintered at 1100, 1300 and 1600°C for three hours. Influence of the different sintering temperatures on the castable properties is discussed. Compressive and flexural strengths were deter mined by destructive testing method, while the water immersion method was used for determination of the bulk density and the water absorption. Changes of elastic properties and microstructure (porosity) were observed by the non-destructive testing methods, ultrasonic measurements and image analysis. Based on the results, it can be concluded that sintering temperature has strong influence on the properties of the LCC. Exceptionally good properties were obtained for the sample sintered at 1600°C, but it should be highlighted that the samples treated at 1100 and 1300°C were provided with good properties, too. This should not be neglected because of the energy saving importance, in cases where the material sintered at lower temperature satisfies the applica tion requirements.